BONDTEX® materials are made to meet these listed specifications and are periodically tested for the above properties. Where conditions of use and/or properties desired are not covered by these listed specifications and laboratory tests, we must be advised of this in writing; so that we can monitor continued product compliance with the amended requirements.

NOTES: 1. Color distribution may vary in solid and multicolor sheets. 2. Gray unless Black specified: AASHTO M-153-67, Type I AASHTO M-153-70, Type I ASTM D-1752-84, Type I HH-F-341-E, Type II, Class A HH-F-341-F, Type II, Class A 3. Based on 50% compression per ASTM D-1752-84 4. Water absorption is intermediate between closed cell and open-cell sponge. Although these materials are made from closed-cell rubber particles, there can be some water absorption into the bonded structure between the individual particles of closed-cellular material. 5. 90% Min. recovery per ASTM D-1752-84 6. Immersion of BONDTEX® materials in gasoline, toluene, naphtha, and similar solvents is not recommended. Surface contacts with these Fluids may cause swelling and softening.

NOTES:
1. Color distribution may vary in solid and multicolor sheets.

2. Gray unless Black specified:
AASHTO M-153-67, Type I
AASHTO M-153-70, Type I
ASTM D-1752-84, Type I
HH-F-341-E, Type II, Class A
HH-F-341-F, Type II, Class A

3. Based on 50% compression per ASTM D-1752-84

4. Water absorption is intermediate between closed cell and open-cell sponge. Although these materials are made from closed-cell rubber particles, there can be some water absorption into the bonded structure between the individual particles of closed-cellular material.

5. 90% Min. recovery per ASTM D-1752-84

6. Immersion of BONDTEX® materials in gasoline, toluene, naphtha, and similar solvents is not recommended. Surface contacts with these Fluids may cause swelling and softening.