BONDTEX®				BONDED RUBBER						SHEETS
Stock Number		913	914	918	920	920-1		925-2	925-3	925-4	925-5	930		941-B	947	950	984	985-1	985-3
Color	(Note 1)	Black	Black	Black	Multicolor	Multicolor		Buff	Gray	Gray	Buff	Black		Black	Black	Black	Black	Black	Black & Natural
Polymer		Neoprene	Neoprene	Neoprene	Blend	Blend		PVC/NBR	PVC/NBR	PVC/NBR	PVC/NBR	Blend		Blend	Neoprene	Blend	PVC/NBR	Blend	Blend
		PVC/NBR		PVC/NBR
Specifications														Note 2
Comp, Deflection (p.s.i.)		2 -10	5 -15	10 - 20	5 -16	15 - 30		30 - 60	30 - 60	30 - 60	30 -60	5 -14		50 - 500	5 -15	8 - 25	1 - 8	4 -12	8 - 25
														Note 3
Density (p.c.f.)		20 -33	22 - 35	25 - 40	15 - 40	20 - 40		25 - 45	25 - 45	25 - 45	25 - 45	20 - 45		30 Min.	25 - 40	25 - 45	15 -25	10 - 36	20 - 45
Water Absorption		Note 4	Note 4	Note 4	Note 4	Note 4		Note 4	Note 4	Note 4	Note 4	Note 4		Note 4	Note 4	Note 4	Note 4	Note 4	Note 4
Temperature Range
Low. High (F')					+10' to 130'	+20' to 130'		+30' to 150'	+30' to 150'	+30' to 150'	+30' to 150'	O' to 150'		+20' to 150'		+20' to 150'	+20' to 130'	+20' to 130'	+30' to 130'
High Intermittent (F')					180'	180'		180'	180'	180'	180'	200'		200'		200'	180'	180'	180'
Compression Set (Max)					30%	30%		20%	20%	20%	20%	30%		Note 5		20%	20%
1/2" sample compressed 50%																		20%	30%
22 hr.. @ 70'F. & 24 hr.. recovery
Heat Aging (7 days@158'F.)					2.0%	2.0%		2.0%	2.0%	2.0%	2.0%	2.0%		2.0%		2.0%	7.0%	4.0%	2.0%
Lineal Shrinkage (Max.)
Tensile Strength (Min. p.s.i.)		13	15	20	13	18		50	50	50	50	20		20	20	20	15	10	20
Elongation (Min.)		40%	40%	50%	50%	30%		50%	50%	50%	50%	40%		60%	50%	50%	20%	40%	50%
Solvent		Note 6	Note 6	Note 6	Note 6	Note 6		Note 6	Note 6	Note 6	Note 6	Note 6		Note 6	Note 6	Note 6	Note 6	Note 6	Note 6

Bondtex® materials are made to meet these listed specifications and are periodically tested for the above properties. Where conditions of use and/or properties desired are not covered by these listed specifications and laboratory tests, we must be advised of this in writing; so that we can monitor continued product compliance with the amended requirements.

 

NOTES:

 

1.     Color distribution may vary in solid and multicolor sheets.                                                                        4.     Water absorption is intermediate between closed cell and open-cell

                                                                                                                                                                                     sponge.  Although these materials are made from closed-cell rubber

2.     Gray unless Black specified:                                                                                                                                particles, there can be some water absorption into the bonded

        AASHTO M-153-67, Type I                                                                                                                                  structure between the individual particles of closed-cellular material.

        AASHTO M-153-70, Type I

        ASTM D-1752-84, Type I

        HH-F-341-E, Type II, Class A                                                                                                                     5.      90% Min. recovery per ASTM D-1752-84

        HH-F-341-F, Type II, Class A        

                                                                                                                                                                            6.      Immersion of Bondtex® materials in gasoline, toluene, naphtha, and

3.     Based on 50% compression per ASTM D-1752-84                                                                                             similar solvents is not recommended. Surface contacts with these

                                                                                                                                                                                     Fluids may cause swelling and softening.